dc.description.abstractNeste trabalho, foram usados dois métodos de síntese, o método de enxerto para modificar a sílica com as aminas aromáticas p-anisidina, p-fenitidina e p-fenilenodiamina e o método sol-gel para obter dois xerogéis híbridos a base de sílica. Um xerogel contendo o grupo orgânico 5-amino-1,3,4-tiadiazol-2-tiol e o outro contendo o 3-aminopropil. Os precursores organossilanos p-anisidinapropiltrimetoxissilano, p-fenitidinapropiltrimetoxissilano, pfenilenodiaminapropiltrimetoxissilano e, 5-amino-1,3,4-tiadiazol-2-tiol propiltrimetoxissilano foram também sintetizados. Foram sintetizadas duas séries de amostras do xerogel 5-amino-1,3,4-tiadiazol-2- tiol/sílica: uma variando-se a quantidade de precursor orgânico adicionado (5,0, 10,0, 20,0 e 40,0 mmol) e a outra variando-se a temperatura de gelificação (50 e 75 ºC). Para o xerogel 3- aminopropil/sílica também foram sintetizadas duas séries de amostras: uma variando-se o tipo de catalisador adicionado e a outra série variando-se o tipo de solvente. Os catalisadores usados foram o HF, HCl, NH4OH e o NH4F enquanto que os solventes estudados foram metanol, etanol, propanol, butanol e pentanol.Na caracterização das sílicas organofuncionalizadas e dos xerogéis híbridos foram usadas as seguintes técnicas: espectroscopia no infravermelho, microscopia eletrônica de varredura, isotermas de adsorção e dessorção de nitrogênio e análise elementar. A potencialidade de aplicação dos materiais híbridos como adsorventes na extração de cátions metálicos em meio aquoso e etanólico foi investigada usando-se isotermas de adsorção pelo método de batelada. Para as sílicas organofuncionalizadas ainda foi realizado um estudo de dessorção e seletividade. A dispersão dos grupos orgânicos na superfície das sílicas organofuncionalizadas ocorreu na forma de monocamada. Essas sílicas foram utilizadas como adsorventes de cátions metálicos, Pb2+, Cu2+, Cd2+ e Ni2+ em soluções aquosas e etanólicas. De modo geral, a capacidade de adsorção obedeceu à seqüência: Pb2+ >> Cu2+ =~ Cd2+ =~ Ni2+. Os estudos de adsorção para esses materias em meio competitivo, mostrou melhor seletividade para Cu2+ e Pb2+ em meio aquoso e Pb2+ em solução etanólica. Quanto aos xerogéis híbridos, observou-se que o aumento no teor de orgânicos resultou em diminuição da área superficial e da porosidade. O aumento da temperatura de gelificação reduziu o tempo de gelificação. O uso de a catálise ácida resultou em materiais híbridos mais compactos, enquanto que a catálise básica produziu materiais com partículas mais esféricas. Osxerogéis sintetizados em álcoois de maiores cadeias foram os que apresentaram os resultados mais promissores para utilização como adsorventes de Cu2+ e Ni2+.pt_BR
dc.description.abstractIn this work, two methods of synthesis were used: grafting to modify silica with the aromatic amines, p-anisidine, p-fenitidine and p-phenylenediamine, and sol-gel to obtain two silica based xerogels, one xerogel that contain the organic group 5-amine-1,3,4-thiadiazole-2- thiol and another with the group 3-aminopropyl. The organic precursors panisidinepropyltrimethoxysilane, p-phenetidinepropyltrimethoxysilane, pphenylenediaminepropyltrimethoxysilane, and 5-amine-1,3,4-thiadiazole-2-thiol propyltrimethoxysilane were also synthesized. Two sample series of the 5-amine-1,3,4-thiadiazole-2-thiol/silica xerogel were synthesized: the first varying the quantity of organic precursor added (5.0, 10.0, 20.0 and 40.0 mmol) and the other one changing the gelation temperature (50 and 75 ºC). For 3- aminopropyl/silica xerogel it was also synthesized two samples series varying the catalyst added and the solvent used. The catalysts used were HF, HCl, NH4OH and NH4F while the solvents employed were methanol, ethanol, propanol, butanol and pentanol. In the characterization of the organofunctionalized silicas and hybrid xerogels the follow techniques were utilized: infrared spectroscopy, scanning electron microscopy, nitrogen adsorption desorption isotherms and elemental analysis.The potentiality to apply the hybrid materials as sorbent for metal cation extraction from aqueous and ethanol solutions was investigated by using adsorption isotherms and batch technique. For the organofunctionalized silicas desorption and selectivity studies was also performed. The organic groups are dispersed on organofunctionalized silicas in a monolayer form. These silicas were used as adsorbents for metal cations Pb2+, Cu2+, Cd2+ and Ni2+ in aqueous and ethanol medium. In a general way, the adsorption capacity values followed the sequence: Pb2+ >> Cu2+ =~ Cd2+ =~ Ni2+. The adsorption studies for these materials in competitive medium showed better selectivity for Cu2+ and Pb2+ in aqueous medium and for Pb2+ in ethanol solution. For the hybrid xerogels, it was observed that the increasing in the organic content results in a decreasing in the surface area and porosity. An increase in the gelation temperature reduced the gelation time. The use of acid catalysis results in compact hybrids, while basic catalysis results in spherical particles. The xerogels synthesized using alcohols with higher chains showed the more promising results for use as Cu2+ and Ni2+ adsorbents.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectSilica organofuncionalizadapt_BR
dc.subjectQuímica inorgânica : Síntesept_BR
dc.subjectSol-gelpt_BR
dc.subjectXerogel híbridopt_BR
dc.titleDesenvolvimento de sílicas organofuncionalizadas para pré-concentração de cátions metálicos em meio aquoso e etanólicopt_BR
dc.typeTesept_BR
dc.contributor.advisor-coBenvenutti, Edilson Valmirpt_BR
dc.identifier.nrb000609434pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentInstituto de Químicapt_BR
dc.degree.programPrograma de Pós-Graduação em Químicapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2007pt_BR
dc.degree.leveldoutoradopt_BR