dc.description.abstractO presente trabalho visa estudar a influência da taxa de resfriamento sobre um aço API 5L-X80, extraído de uma seção circular de duto, soldado com o processo MAG automatizado e com dois arames, um maciço e um arame tubular de alma metálica. Para a obtenção de diversas taxas de resfriamento, cinco distintos pré-aquecimentos foram utilizados. Preliminarmente foram realizadas soldas de simples deposição de metal sobre uma seção do duto, com o objetivo de estudar as transformações metalúrgicas na Zona Afetada pelo Calor (ZAC) e no metal de solda. A seguir foram soldados, com cinco diferentes temperaturas de pré-aquecimento e de interpasse, chanfros duplo V com nariz. As soldagens de simples deposição de metal foram analisadas com o uso de Microscópio de Luz, Microscópio Eletrônico de Varredura e Dureza. Sobre os chanfros soldados, as propriedades mecânicas e metalúrgicas foram avaliadas com os ensaios de Tração, Dobramento, Impacto (Charpy-V) e Dureza (Vickers). Os resultados dos testes mecânicos foram superiores aos mínimos definidos por norma, com resultados muito interessantes. Houve uma boa correlação entre os testes de dureza, tração e ensaio de impacto. Os ensaios mecânicos em conjunto com as análises metalúrgicas demonstraram que o efeito combinado do tempo e temperatura, criaram grandes alterações nos resultados. As propriedades mecânicas das juntas soldadas foram superiores as mínimas exigidas pela norma API 5L.pt_BR
dc.description.abstractThis work aims to study the cooling rate effects on an API 5L-X80 steel (circular hollow section) welded with automatized GMAW and with two distinct wires one solid and one metal cored. In order to obtain different cooling rates, five distinct pre-heatings were utilized. At first, beads on plate welds were made, on a section of the pipeline, as a preliminary study of the metallurgical alterations in the Heat Affected Zone (HAZ) and in the weld metal. Also, five double V grooves were welded, using different preheating and interpass temperatures. On the beads on plate welds were evaluated metallurgical and metallurgical properties through Light Microscope, Scanning Electron Microscope and hardness. On the welded grooves, the mechanical properties were evaluated through Tensile, Bending, Impact (Charpy-V) and Hardness (Vickers) tests. The results of mechanical tests were above the minimum defined by standard, with very interesting results. There was a good correlation between the hardness testing, tensile and impact testing. The mechanical tests together with metallurgical analysis showed that the combined effect of time and temperature, created huge changes in the results. The mechanical properties of the welded joints were higher than the minimum required by the standard API 5L.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectSoldagempt_BR
dc.subjectWeldingen
dc.subjectAPI 5L-X80 steelen
dc.subjectAçopt_BR
dc.subjectEnsaios mecânicospt_BR
dc.subjectImpact resistanceen
dc.subjectCooling ratesen
dc.titleSoldagem de um aço API 5L-X80 com diferentes taxas de resfriamentopt_BR
dc.title.alternativeWelding of an API 5L-X80 pipeline steel with different cooling rates en
dc.typeDissertaçãopt_BR
dc.identifier.nrb000967032pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2015pt_BR
dc.degree.levelmestradopt_BR