dc.description.abstractO protocolo moderno de tratamento da doença cárie está baseado na intervenção minimamente invasiva, que pode lançar mão da remoção parcial de tecido cariado para reduzir os riscos de problemas pós-operatórios. Por possuir capacidade de aderir aos subtratos dentários, os cimentos de ionômero de vidro apresentam indicação para esse processo. Em contrapartida, fosfatos cálcicos apresentam potencialidade de induzir deposição mineral. Sendo assim, o objetivo desse estudo foi avaliar o efeito da incorporação de fosfato octacálcico (OCP), α-fosfato tricálcico (α-TCP) ou hidroxiapatita (HA) sobre as propriedades de um cimento de ionômero de vidro comercial restaurador, bem como caracterizar a dentina bovina desmineralizada restaurada com esses materiais. Foram produzidos três grupos testes: GOCP, GTCP e GHA, por meio da substituição de 5% em massa do pó do cimento original, por 5% em massa de OCP, de α-TCP ou de HA, respectivamente. O grupo GCIV, sem alterações, foi o grupo controle. As propriedades avaliadas foram radiopacidade, tempo de presa inicial e profundidade de polimerização, de acordo com a ISO 9917-2:2010. A caracterização da dentina foi realizada através de microdureza Knoop e espectrocopia Raman, através da intensidade do pico 962 cm-1, para verificar-se a presença de fosfato no interior da dentina. Os resultados de radiopacidade foram equivalentes a 3 mmAl. O tempo de presa inicial variou entre 39,06 + 1,15 min, para o GCIV, e 58,39 + 2,64 min, para o GTCP. Na profundidade de polimerização, os valores variaram entre 1,61 + 0,04, para o GHA, e 1,77 + 0,04 mm, para o GTCP. Todos os resultados de radiopacidade, tempo de presa inicial e profundidade de polimerização foram de acordo com os preconizados pela norma. A dureza da dentina hígida foi superior tanto à dureza dos grupos que foram submetidos à restauração quanto à dureza da dentina desmineralizada. Mesmo sendo ilustrativas, as imagens obtidas da dentina dos diferentes grupos mostram intensidades variadas de fosfato, especialmente em relação à dentina hígida, permitindo inferir que, dentre os grupos desmineralizados, há maior intensidade no GHA. Pode-se concluir que a adição de fosfatos cálcicos não prejudicou as propriedades do cimento de ionômero de vidro comercial e que as imagens que representam a intensidade de fosfato no interior da dentina dos grupos sugerem que os materiais avaliados podem apresentar uma potencial ação indutora de deposição mineral.pt_BR
dc.description.abstractThe modern protocol for treating caries disease is based on minimal invasive intervention, which can employ incomplete caries removal, to reduce post-operatory problems. For bearing capacity to adhere to tooth substrate, the glass ionomer cement is indicated for this process. Furthermore, the calcium phosphates have potential to induce mineral deposition. Thus, the aim of this study was to evaluate the effect of the addition of octacalcium phosphate (OCP), αtricalcium phosphate (α-TCP), or nanostructured hydroxyapatite (HA) on the properties of commercial restorative glass ionomer cement, and to characterize demineralised bovine dentin restored with these materials. Three test groups were produced: GOCP, GTCP, and GHA, through the substitution of 5%, by mass, of original cement powder with 5%, by mass, of OCP, α-TCP or HA, respectively. The group GCIV, without alteration, was the control group. Radiopacity, initial hardening time, and depth of cure were the properties evaluated, all according to ISO 9917-2:2010. Dentin characterization was conducted using Knoop microhardness and Raman spectroscopy, through 962 cm-1 intensity peak, to verify phosphate existence in inner dentin. Radiopacity results were equivalent to 3 mmAl. Initial hardening time varied between 39.06 + 1.15 min, for GCIV, and 58.39 + 2.64 min, for GTCP. For depth of cure, values varied between 1.61 + 0.04 mm, for GHA, and 1.77 + 0.04 mm, for GTCP. All results of radiopacity, initial hardening time and depth of cure were according to what is established by the standard. Hard sound dentin values were superior both for restored groups hardness and for demineralised dentin hardness. Though illustrative, different groups dentin images show varied phosphate intensities, especially regarding sound dentin, allowing to infer that, among demineralised groups, there are higher intensity in GHA. Thus, it is possible to conclude that the addition of calcium phosphates did not impaired commercial glass ionomer cement properties and that groups images representing inner dentin phosphate intensity suggest that evaluated materials may present potential mineral deposition induction action.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectMateriais biocompatíveispt_BR
dc.subjectGlass ionomer cementsen
dc.subjectCimentos dentáriospt_BR
dc.subjectTooth remineralizationen
dc.subjectDental cariesen
dc.subjectFosfatos de cálciopt_BR
dc.titleInfluência da adição de fosfato octacálcico, alfa-fosfato tricálcico ou hidroxiapatita nas propriedades de um cimento de ionômero de vidropt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000971386pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Odontologiapt_BR
dc.degree.programPrograma de Pós-Graduação em Odontologiapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2015pt_BR
dc.degree.levelmestradopt_BR