Ionic liquid intercalated V2O5 nanorods : synthesis and characterization

.

Ionic liquid intercalated V2O5 nanorods : synthesis and characterization

Mostrar registro completo

Estatísticas

Título Ionic liquid intercalated V2O5 nanorods : synthesis and characterization
Autor Manjunath, K.
Souza, Virgínia Serra de
Dupont, Jairton
Ramakrishnappa, Thippeswamy
Nagaraju, Ganganagappa
Abstract In this work, ionic liquid (IL) intercalated V2O5 (IL-V2O5) nanorods have been synthesized through the IL-assisted hydrothermal method using imidazolium-based functionalized IL at 130°C for 3 days. The structure and morphology of the obtained product was characterized using various techniques. X-ray diffraction pattern reveals the intercalation of IL at 2θ = 7° in orthorhombic V2O5. The Fourier transform infrared spectrum shows a band at 1044 cm–1, which could be assigned to stretching vibration of terminal vanadyl (V=O), sensitive to cation intercalation between vanadium oxide layers. UV–vis absorption spectrum of IL-V2O5 nanorods and calcined V2O5 nanoparticles show a maximum absorbance at 402 and 420 nm, respectively. The morphology of the product was investigated by scanning electron microscopy and transition electron microscopy (TEM). TEM analysis reveals the nanorods with thickness of 30–50 nm.
Contido em Bulletin of Materials Science. India. Vol. 38, no. 5 (Sept. 2015), p. 1309-1313
Assunto Líquidos iônicos
Nanobastões
Nanoparticulas
Nanotecnologia
Pentóxido de vanádio
Origem Estrangeiro
Tipo Artigo de periódico
URI http://hdl.handle.net/10183/131278
Arquivos Descrição Formato
000981269.pdf (1.471Mb) Texto completo (inglês) Adobe PDF Visualizar/abrir

Este item está licenciado na Creative Commons License

Este item aparece na(s) seguinte(s) coleção(ões)


Mostrar registro completo

Percorrer



  • O autor é titular dos direitos autorais dos documentos disponíveis neste repositório e é vedada, nos termos da lei, a comercialização de qualquer espécie sem sua autorização prévia.
    Projeto gráfico elaborado pelo Caixola - Clube de Criação Fabico/UFRGS Powered by DSpace software, Version 1.8.1.