dc.description.abstractO objetivo do presente estudo foi desenvolver cimentos endodônticos resinosos a base de bisfenol A glicidil dimetacrilato etoxilado com adição de diferentes radiopacificantes em diferentes concentrações e caracterizá-los quanto às propriedades relacionadas a um cimento endodôntico. Foram desenvolvidos cimentos endodônticos resinosos pasta/pasta experimentais a base de BisEMA e neles foi incorporado Canforoquinona, EDAB, DHEPT, BHT e Peróxido de Benzoila. Para formar os grupos experimentais, foram adicionados WCaO4, YbF3 ou Ta2O5 nas concentrações de 20, 40, 60, 80 e 100%. Após o desenvolvimento dos cimentos, foram realizados os ensaios laboratoriais para avaliar as seguintes propriedades: escoamento, espessura de filme e radiopacidade, conforme as orientações da ISO 6876, de 2001, sorção e solubilidade, de acordo com a ISO 4049, de 2009, pH, utilizando um pHmetro e grau de conversão, por meio de infravermelho por transformada de Fourier. No teste de escoamento, todos os grupos apresentaram menor escoamento quanto maior a quantidade de carga presente. No teste de espessura de filme, nenhum grupo ultrapassou os 50 μm, como recomendado pela ISO, exceto o grupo WCaO4100%, que obteve 76,7 (±15,3). O pH variou de 5,95 (±0,07), do YbF380%, a 6,90 (±0,07), do Ta2O580%. No ensaio de radiopacidade, os grupos YbF360%, Ta2O580% e Ta2O5100% apresentaram valores estatisticamente semelhante a 3 mmAl. Os grupos Ta2O5 e YbF3 nas concentrações de 40 e 60% apresentaram valores de sorção e solubilidade recomendados pela ISO 4049. Com adição de Ta2O5 e WCaO4 diminuiu o grau de conversão em 14 dias. Sendo assim, o grupo YbF360% obteve resultados promissores para utilização como um cimento endodôntico.pt_BR
dc.description.abstractThe aim of the study was to develop Bisphenol A ethoxylated dimethacrylate resin based root canal sealers adding different fillers in different concentrations and characterize them as endodontic sealers properties. The experimental BisEMA resin based endodontic sealers were produced using Camphoroquinone, EDAB, DHEPT, BHT and benzoyl peroxide. The experimental groups were formulated adding 20, 40, 60, 80 and 100% of WCaO4, YbF3 or Ta2O5. After producing the sealers, flow, thickness and radiopacity tests were conducted in accordance with ISO 6876. Sorption and solubility tests were conducted in accordance with ISO 4049, pH was measure with a pHmeter and degree of conversion was evaluated with Fourier Transform Infrared Spectroscopy (FTIR). All groups showed lower flow with increased filler concentration. All groups showed film thickness values lower than 50 μm, as ISO recommends, except WCaO4100% group (76,7). pH values varied from 5,95 (±0,07), YbF380% group, to 6,90 (±0,07), Ta2O580% group. In the radiopacity test, YbF3 60%, Ta2O580% and Ta2O5100% groups showed no statistical significant difference to 3 mmAl. Ta2O5 and YbF3 groups in 40 and 60% concentrations presented sorption and solubility values as ISO 4049 recommendation. Adding Ta2O5 and WCaO4, the conversion degree decreased in 14 days. Therefore, YbF360% group obtained promising results for using as a root canal sealer.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectCimentospt_BR
dc.subjectCanals sealeren
dc.subjectMateriais odontologicos : Avaliacaopt_BR
dc.subjectDentistryen
dc.titleInfluência da adição de diferentes partículas de carga em um cimento endodôntico experimental a base de BisEMApt_BR
dc.title.alternativeInfluence of different fillers addition in an experimental BisEMA based root canal sealer en
dc.typeTrabalho de conclusão de graduaçãopt_BR
dc.identifier.nrb000829017pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentFaculdade de Odontologiapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2011pt_BR
dc.degree.graduationOdontologiapt_BR
dc.degree.levelgraduaçãopt_BR


Thumbnail
   

Este item está licenciado na Creative Commons License

Mostrar registro simples