Estudo da perfuração de chapas grossas de aço ASTM A-36

.

Estudo da perfuração de chapas grossas de aço ASTM A-36

Mostrar registro completo

Estatísticas

Título Estudo da perfuração de chapas grossas de aço ASTM A-36
Autor Antunes, Filipe
Orientador Schaeffer, Lirio
Co-orientador Castelan, Jovani
Data 2017
Nível Mestrado
Instituição Universidade Federal do Rio Grande do Sul. Escola de Engenharia. Programa de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiais.
Assunto Chapas de aço
Punção (Engenharia)
[en] AISI D2
[en] AISI S1
[en] Punching process
[en] Shear punch
Resumo O presente trabalho estuda a variação do diâmetro inicial e diâmetro final de um furo puncionado feito em uma chapa de aço ASTM A-36 com 12,7 mm de espessura. São propostas três geometrias diferentes de punção fabricados em aço AISI D2 e AISI S1 com diâmetro inicial 20 mm e final 22 mm. Os punções foram fabricados para realizarem o processo de puncionamento e brochamento com penetrações de avanço (asf) de 0,2 mm, 0,5 mm e 1 mm. O objetivo principal é reduzir a conicidade dos furos puncionados atualmente através do método convencional. As folgas entre punção e matriz (w) utilizadas foram de 3,1%, 7,8% e 15,7% da espessura da chapa de testes respectivamente. Para avaliação do desempenho de cada ferramenta, todos os furos puncionados foram medidos e tabelados. Entre os resultados encontrados, constatou-se que os punções com brochamento apresentam melhores valores que os convencionais em todos parâmetros analisados. As regiões de cisalhamento (Zc) e região de ruptura abrupta (Zr) também sofreram influência direta em função da geometria utilizada.
Abstract The present work studies the variation of the initial diameter and final diameter of a punched hole made in an ASTM A-36 steel sheet with 12.7 mm of thickness. Three different punches geometries are proposed and manufactured from AISI D2 and AISI S1 steel with initial diameter 20 mm and final diameter 22 mm. The punches were manufactured to carry out the punching and broaching process with feed penetrations (asf) of 0.2 mm, 0.5 mm and 1 mm. The main objective is to reduce the conicity of the punched holes currently through the conventional method. The clearance between punch and die (w) used were 3.1%, 7.8% and 15.7% of the thickness of the test plate respectively. To evaluate the performance of each tool, all punched holes were measured and tabulated. Among the results, it was observed that the punches with a broaching showed better values than the conventional ones in all analyzed parameters. The regions of shear (Zc) and region of abrupt rupture (Zr) also had a direct influence in function of the geometry used.
Tipo Dissertação
URI http://hdl.handle.net/10183/173781
Arquivos Descrição Formato
001061690.pdf (2.829Mb) Texto completo Adobe PDF Visualizar/abrir

Este item está licenciado na Creative Commons License

Este item aparece na(s) seguinte(s) coleção(ões)


Mostrar registro completo

Percorrer



  • O autor é titular dos direitos autorais dos documentos disponíveis neste repositório e é vedada, nos termos da lei, a comercialização de qualquer espécie sem sua autorização prévia.
    Projeto gráfico elaborado pelo Caixola - Clube de Criação Fabico/UFRGS Powered by DSpace software, Version 1.8.1.