Dual catalyst system composed by nickel and vanadium complexes containing nitrogen ligands for ethylene polymerization

.

Dual catalyst system composed by nickel and vanadium complexes containing nitrogen ligands for ethylene polymerization

Mostrar registro completo

Estatísticas

Título Dual catalyst system composed by nickel and vanadium complexes containing nitrogen ligands for ethylene polymerization
Autor Furlan, Luciano Gomes
Casagrande Júnior, Osvaldo de Lázaro
Resumo Blendas de polietileno ramificado/polietileno de alta densidade (BPE/HDPE) foram preparadas usando uma combinação de catalisadores [NiCl2(diimina-α)] (1) (diimina-α = 1,4-bis(2,6- diisopropilfenila)-acenafeteno) e [TpMs*VCl2(NtBu)] (2) (TpMs* = hidridobis(3-mesitilapirazol-1- il)(5-mesitilapirazol-1-il)). As reações de polimerização foram realizadas em hexano ou tolueno em três diferentes temperaturas (0, 30 e 50 °C), utilizando várias razões molares de níquel (xNi), na presença de metilaluminoxano (MAO) como cocatalisador. Em todas as temperaturas, as atividades mostraram uma correlação aproximadamente linear com xNi, indicando o não aparecimento de um efeito sinérgico entre as espécies de níquel e vanádio. Altas atividades foram obtidas a 0 °C. As temperaturas de fusão (Tm) das blendas de polietileno produzidas a 0 °C diminuem conforme a xNi aumenta no meio reacional, indicando uma boa miscibilidade entre as fases de polietileno produzidas por ambos catalisadores. A morfologia da superfície das blendas de BPE/HDPE estudadas por microscopia eletrônica de varredura (MEV) revelou uma baixa miscibilidade entre as fases de PE, principalmente no caso das blendas poliméricas produzidas a alta temperatura (50 ºC).
Abstract Branched polyethylene/high-density polyethylene blends (BPE/HDPE) were prepared using the combined [NiCl2(α-diimine)] (1) (α-diimine = 1,4-bis(2,6-diisopropylphenyl)- acenaphthenediimine) and [TpMs*VCl2(NtBu)] (2) (TpMs* = hydridobis(3-mesitylpyrazol-1-yl)(5- mesitylpyrazol-1-yl)) catalysts. The polymerization reactions were performed in hexane or toluene at three different polymerization temperatures (0, 30 and 50 °C) and several nickel molar fractions (xNi), using MAO as cocatalyst. At all temperatures, the activities show an approximate linear correlation with xNi, indicating a non-synergistic effect between the nickel and the vanadium species. Higher activities were found in toluene at 0 °C. The melting temperatures for the polyethylene blends produced at 0 °C decrease as xNi increases in the medium indicating good miscibility between the polyethylene phases made by both catalysts. The surface morphology of the BPE/HDPE blends studied by scanning electron microscopy (SEM) revealed low miscibility between the PE phases mainly in the case of the polymer blends produced at high temperature (50 ºC).
Contido em Journal of the Brazilian Chemical Society. São Paulo. Vol. 16, n. 6A (2005), p. 1248-1254
Assunto Blendas de polímeros
Catalisadores : Níquel
Catalisadores : Vanádio
Etileno : Polimerizacao
[en] BPE/HDPE blends
[en] Ethylene polymerization
[en] Homogeneous binary catalyst system
[en] Nickel and Vanadium catalysts
Origem Nacional
Tipo Artigo de periódico
URI http://hdl.handle.net/10183/24562
Arquivos Descrição Formato
000528739.pdf (757.6Kb) Texto completo (inglês) Adobe PDF Visualizar/abrir

Este item está licenciado na Creative Commons License

Este item aparece na(s) seguinte(s) coleção(ões)


Mostrar registro completo

Percorrer



  • O autor é titular dos direitos autorais dos documentos disponíveis neste repositório e é vedada, nos termos da lei, a comercialização de qualquer espécie sem sua autorização prévia.
    Projeto gráfico elaborado pelo Caixola - Clube de Criação Fabico/UFRGS Powered by DSpace software, Version 1.8.1.