UHMWPE-layered silicate nanocomposites by in situ polymerization with tris(pyrazolyl)borate titanium/clay catalyst

.

UHMWPE-layered silicate nanocomposites by in situ polymerization with tris(pyrazolyl)borate titanium/clay catalyst

Mostrar registro completo

Estatísticas

Título UHMWPE-layered silicate nanocomposites by in situ polymerization with tris(pyrazolyl)borate titanium/clay catalyst
Autor Junges, Fernando
Beauvalet, Mariana Silva
Leal, Bárbara Caroline
Casagrande, Adriana Curi Aiub
Mota, Fabio Fernandes
Mauler, Raquel Santos
Casagrande Júnior, Osvaldo de Lázaro
Resumo Nanocompósitos de polietileno-MMT foram preparados através da metodologia de polimerização in situ utilizando TpMs*TiCl3 (1) intercalado na galeria da Cloisite 30B (C30B) e na presença de metilaluminoxano (MAO) como ativador. Através da análise de difração de raios-X (DRX) foi observado que o espaçamento basal da argila ativada muda de 1,85 nm (2θ = 4,8) para 2,18 nm (2θ = 4,0) indicando a ocorrência da intercalação do catalisador de titânio na galeria da argila. O sistema catalítico 1/C30B/MAO foi ativo na polimerização do etileno sob diferentes condições reacionais. A morfologia esfoliada do nanocompósito PE-MMT foi confirmada pela análise de difração de raios-X (DRX) e microscopia eletrônica de transmissão (MET). A presença de argila esfoliada (5% em peso) na matriz polimérica confere melhores propriedades mecânicas (módulo de flexão e módulo de armazenamento) quando comparada com aquelas apresentadas pelo polietileno puro produzido exclusivamente por 1.
Abstract Polyethylene-MMT nanocomposites were prepared by in situ polymerization methodology using TpMs*TiCl3 (1) intercalated into the gallery of Cloisite 30B (C30B) using methylaluminoxane (MAO) as activator. From the powder X-ray diffraction (XRD) analysis it was observed that the basal spacing of the activated organoclay changes from 1.85 nm (2θ = 4.8) to 2.18 nm (2θ = 4.0) indicating that the intercalation of the titanium catalyst into the gallery took place. The catalytic system 1/C30B/MAO was active in the ethylene polymerization under different reaction conditions. The exfoliated morphology of the PE-MMT nanocomposite was further examined and confirmed by X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis. The presence of exfoliated clay (5 wt.%) in the PE matrix confers better mechanical properties (flexural modulus and storage modulus) when compared with the ones displayed by the neat PE produced using exclusively 1.
Contido em Journal of the Brazilian Chemical Society. São Paulo. Vol. 20, n. 3 (2009), p. 472-477
Assunto Catalisadores : Titânio
Cerâmica
Nanocompósitos
Polímeros
[en] Clay
[en] Nanocomposites
[en] Titanium catalyst
[en] UHMWPE
Origem Nacional
Tipo Artigo de periódico
URI http://hdl.handle.net/10183/24593
Arquivos Descrição Formato
000705593.pdf (350.2Kb) Texto completo (inglês) Adobe PDF Visualizar/abrir

Este item está licenciado na Creative Commons License

Este item aparece na(s) seguinte(s) coleção(ões)


Mostrar registro completo

Percorrer



  • O autor é titular dos direitos autorais dos documentos disponíveis neste repositório e é vedada, nos termos da lei, a comercialização de qualquer espécie sem sua autorização prévia.
    Projeto gráfico elaborado pelo Caixola - Clube de Criação Fabico/UFRGS Powered by DSpace software, Version 1.8.1.