dc.description.abstractPelo processo MIG/MAG foram efetuados depósitos de solda utilizando-se várias misturas de proteção, envolvendo argônio, oxigênio e dióxido de carbono, visando verificar a influência do gás sobre as propriedades mecânicas do metal de solda de baixo carbono. Posteriormente, mediante nova série de soldas, foi estudado o efeito destes gases nas taxas de deposição do processo e na geometria do cordão. Com o objetivo de obter-se dados confiáveis, construiu-se um dispositivo destinado à mecanização do processo de soldagem. Foi possível, desta forma, analisar-se unicamente o efeito do gás nos experimentos. Os resultados indicaram que misturas com menores quantidades de 02 e CO2 possibilitaram valores mais elevados de tenacidade, tanto a altas como a baixas temperaturas, provavelmente devido aos reduzidos teores de oxigênio no metal de solda e à presença de uma maior quantidade de ferrita acicular. No tocante à resistência à tração, escoamento e alongamento, não foram constatadas diferenças substânciais pela variação do gás de proteção. Igualmente nas taxas de deposição do processo, não tivemos alterações de significado. No estudo da geometria do cordão de solda, verificou-se que o gás de proteção provocou variações, destacando-se, porém, que misturas envolvendo dióxido de carbono e oxigênio (4 a 15%) podem garantir maior penetração.pt_BR
dc.description.abstractWeld deposits were nade with MIG/MAG process using some shielding gas mixtures with different contents of argon, oxygen and carbon dioxide. They were used to investigate the gases influence on mechanical properties of low carbon steel weld metal. After that, weld beads were deposited to study the effect of theses mixtures on the weld shape and penetration patterns. In order to evaluate only the effect of shielding gas, the deposits were made using an automatic welding machine. The results indicated that mixtures with low quantities of 02 and CO2 produce weld metals with higher toughness at high and low temperatures. Probably it was due to the low contents of oxygen in weld metal and the great amount of acicular ferrite. There was practically no differences in ultimate tensile strenght, yield strenght and alongation by changing the shielding gas. Also, the tests indicate that deposition rates were similar. It was noted that the gas affected the shape of weld bead and penetration patterns. Mixtures with carbon dioxide and oxygen (4 to 15%) improved the penetration.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectSoldagem MIG/MAGpt_BR
dc.subjectSoldagem a arco elétricopt_BR
dc.titleInfluência dos gases de proteção utilizados no processo MIG/MAG sobre as propriedades mecânicas do metal de soldapt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000062837pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia Metalurgica e dos Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date1990pt_BR
dc.degree.levelmestradopt_BR


Thumbnail
   

Este item está licenciado na Creative Commons License

Mostrar registro simples