dc.description.abstractO presente trabalho estuda a conformação da liga de magnésio AZ61 pelos processos de extrusão direta e forjamento, ambos a quente. No processo de extrusão, são submetidos à conformação corpos-de-prova da liga de magnésio AZ61 nos estados fundido e recristalizado. As geometrias de ferramenta são variadas e a influência destas variações sobre a força de processamento e propriedades mecânicas e microestrutura do material são analisada. Demonstra-se que a liga no estado inicialmente recristalizado tem propriedades mecânicas finais superiores à liga inicialmente fundida, embora demande de maior força de processamento. Demonstra-se também que a geometria de ferramenta tem influência sobre as respostas mecânicas obtidas das peças após extrusão. Referente ao processo de forjamento, a liga de magnésio AZ61 é processada apenas no estado recristalizado, variando-se a temperatura e o número de tapas de forjamento. Foi avaliada a influência destas variações de processo nas propriedades mecânicas finais da peça. Ao fim, percebe-se que ao se forjar as peças com múltiplas etapas de forjamento e temperaturas decrescentes, impede-se a recristalização do material, alcançando alto encruamento dos grãos, o que gera, na peça final, propriedades mecânicas superiores ao processo convencional.pt_BR
dc.description.abstractThis thesis studies the deformation of a magnesium alloy AZ61 by forward extrusion and forging processes, at elevated temperatures. In the extrusion process, the samples were deformed in as cast and recrystallized conditions. The tools geometries were variated and the influences on processing force, mechanical properties and material microstructure were analyzed. Was found that the recrystallized samples have better mechanical properties than as cast samples, after extruded, although it requires more processing force. Also was found that the tool geometry influences on mechanical properties and microstructure of extruded magnesium alloy. Relatively to the forging process, magnesium alloy AZ61 was processed only in the recrystallized state, varying the process temperature and the number of forging steps. Aimed to evaluate the process variations influences on the mechanical properties and microstructure of the final parts. At the end, was observed that when forging parts with multi-step forging and decreasing temperatures, to prevent recrystallization of the material, achieving high strain hardening of the grains, which results in final part with superior mechanical properties to the conventional process.en
dc.format.mimetypeapplication/pdf
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectAZ61 magnesium alloyen
dc.subjectLigas de magnésiopt_BR
dc.subjectForjamentopt_BR
dc.subjectForward extrusion of magnesium alloyen
dc.subjectExtrusãopt_BR
dc.subjectForging process of magnesium alloyen
dc.titleDesenvolvimento e controle de processos de conformação da liga de magnésio AZ61pt_BR
dc.typeTesept_BR
dc.identifier.nrb000835359pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentEscola de Engenhariapt_BR
dc.degree.programPrograma de Pós-Graduação em Engenharia de Minas, Metalúrgica e de Materiaispt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date2012pt_BR
dc.degree.leveldoutoradopt_BR


Thumbnail
   

Este item está licenciado na Creative Commons License

Mostrar registro simples