Electrical isolation of p-type GaAs layers by ion irradiation

.

Electrical isolation of p-type GaAs layers by ion irradiation

Mostrar registro completo

Estatísticas

Título Electrical isolation of p-type GaAs layers by ion irradiation
Autor Boudinov, Henri Ivanov
Coelho, Artur Vicente Pfeifer
Souza, Joel Pereira de
Abstract The electrical isolation of p-type GaAs layers doped with acceptor impurities incorporated in the Ga sublattice (Mg) or As sublattice (C) was studied using proton bombardment. It was found that practically the same proton dose is required to reach complete isolation (isolation threshold dose, Dth) in layers doped with either Mg or C of comparable original sheet hole concentration (ps). This result is evidence that the sublattice where the acceptor dopant atoms are incorporated does not play any significant role for the isolation formation process in GaAs. The behavior of the recovery of the conductivity during subsequent thermal annealing was found very similar in Mg and C doped samples irradiated to equal proton doses. In samples irradiated to doses <Dth, the sheet resistance (Rs) increases during annealing at temperatures >100°C, reaches a maximum at ~≈200°C, and then decreases progressively toward the original value. For proton doses ranging from Dth to 5Dth , the isolation is preserved up to the temperature of ~≈500°C. The temperature of ~≈700°C was found to be the upper limit for the thermal stability of the isolation in samples irradiated to doses of 100 Dth.
Contido em Journal of applied physics. Melville. Vol. 91, no. 10 (May 2002), p. 6585-6587
Assunto Arseneto de galio
Carbono
Condutividade
Condutividade eletrica
Magnesio
Semicondutores iii-v
Origem Estrangeiro
Tipo Artigo de periódico
URI http://hdl.handle.net/10183/95818
Arquivos Descrição Formato
000323332.pdf (202.3Kb) Texto completo (inglês) Adobe PDF Visualizar/abrir

Este item está licenciado na Creative Commons License

Este item aparece na(s) seguinte(s) coleção(ões)


Mostrar registro completo

Percorrer



  • O autor é titular dos direitos autorais dos documentos disponíveis neste repositório e é vedada, nos termos da lei, a comercialização de qualquer espécie sem sua autorização prévia.
    Projeto gráfico elaborado pelo Caixola - Clube de Criação Fabico/UFRGS Powered by DSpace software, Version 1.8.1.