Stress level in finemet materials studied by impedanciometry

.

Stress level in finemet materials studied by impedanciometry

Mostrar registro completo

Estatísticas

Título Stress level in finemet materials studied by impedanciometry
Autor Carara, Marcos Andre
Baibich, Mario Norberto
Sommer, Rubem Luis
Abstract In this work, a study of the stress relief in Finemet ribbons, Fe73.5Cu1Nb3Si16.5B6, as a function of the annealing temperature is presented. The as melt-spun samples are amorphous and become partially crystallized after annealing at appropriate temperatures. For temperatures TA≥480°C the samples are nanocrystalline, with a microstructure composed by α-Fe12xSix(x~0.2) crystallites (10 nm average diameter) embedded in an amorphous matrix. Nanocrystallization, associated with stress relief effects, improves the soft magnetic properties of this kind of material. The stress level was quantified using magnetorestriction (measured by SAMR), magnetoelastic anisotropy, and domain wall energy data obtained from impedance spectra measurements. A reduction of the internal stress from 15 to 0.2 MPa was verified when comparing the as-cast to the sample annealed at 580°C. Improvement of the magnetic softness of the samples was also followed by the increase of the domain wall and magnetization rotation contributions to the overall effective permeability.
Contido em Journal of applied physics. Melville. Vol. 91, no. 10 (May 2002), p. 8441-8443
Assunto Cristalização
Efeitos magnetoelasticos
Impedância elétrica
Ligas de boro
Ligas de cobre
Ligas de ferro
Materiais amorfos magnéticos
Materiais ferromagneticos
Materiais nanoestruturados
Paredes de domínios magnéticos
Permeabilidade magnética
Recozimento
Tensões internas
Origem Estrangeiro
Tipo Artigo de periódico
URI http://hdl.handle.net/10183/95819
Arquivos Descrição Formato
000323336.pdf (200.1Kb) Texto completo (inglês) Adobe PDF Visualizar/abrir

Este item está licenciado na Creative Commons License

Este item aparece na(s) seguinte(s) coleção(ões)


Mostrar registro completo

Percorrer



  • O autor é titular dos direitos autorais dos documentos disponíveis neste repositório e é vedada, nos termos da lei, a comercialização de qualquer espécie sem sua autorização prévia.
    Projeto gráfico elaborado pelo Caixola - Clube de Criação Fabico/UFRGS Powered by DSpace software, Version 1.8.1.