dc.description.abstractA borracha estireno-butadieno (SBR) e as borrachas acrilonitrila - butadieno (NBR) com diferentes teores de acrilanitrila (15%, 28% e 45% em mol) foram modificadas corn 4 - fenil-1, 2, 4-triazolina-3,5-diona ( P T D ). As propriedades em solução - viscosidade intrínseca e cromatagráfica de permeação em gel - e a propriedade mecânica de tensão-deformação destes materiais foram estudadas antes e depois da adição de grupos polares, capazes de interagir via pontes de hidrogênio, à cadeia polimérica. A formação destes complexos de ligação de hidrogênio influenciam marcadamente essas propriedades. Para NBR, a variacão das propriedades depende da quantidade de acrilanitrila. Ligas de NBR/SBR modificadas e não modificadas foram obtidas e a compatibilidade dos componentes analisada através da temperatura de transição vítrea determinada por calorimetria de varredura diferencial. Houve uma melhora miscibilidade dos componentes com a modificação. As propriedades mecânicas (tensão-de-formação) destes sistemas foram estudadas em relação a variação da composição e grau de modificação das componentes em cada tipo de borracha nitrílica. Ligas de SBR/NBR modificadas e SBR modificada/NBR não modificada apresentaram propriedades mecânicas superiores a de sues componentes puros (sinergismo).pt_BR
dc.description.abstractStyrene-butadiene rubber ( SBR ) and acrylonitrile-butadiene rubbers (NBR) with differents contents of acrylonitrile (15%, 28% and 45% mole) were modified with 4-phenyl-1,2,4-triazoline-3,5-dione (PTD). The solution properties - intrinsic viscosity and gel permeation chromatography - and the stress-strain properties of these materials were studied before and after the addition of polar groups to the polymer backbone. The hydrogen bond complexes formation, by these polar groups, influences strongly these properties. Modified and unmodified NBR/SBR blends were prepared and their degree of compatibility analyzed by Differential Scanning Calorimetry (glass transition temperature). It was observed an increase in the components miscibility upon modification. The stress strain properties of these systems were studied in relation to the composition variation and degree of modification of the components for each type of nitrile rubber. As a consequence of the hydrogen bonding formation, NBR/SBR modified and NBR unmodified/SBR modified blends showed superior stress-strain properties as compared to either of the modified components (synergism).en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoporpt_BR
dc.rightsOpen Accessen
dc.subjectPontes de hidrogeniopt_BR
dc.subjectLigas elastoméricaspt_BR
dc.subjectPolímeros : Purificaçãopt_BR
dc.subjectPolímeros : Caracterizaçãopt_BR
dc.subjectPolimeros : Modificacaopt_BR
dc.titleInfluência de ligações de hidrogênio sobre as propriedades de elastômeros e ligas elastoméricaspt_BR
dc.typeDissertaçãopt_BR
dc.identifier.nrb000019230pt_BR
dc.degree.grantorUniversidade Federal do Rio Grande do Sulpt_BR
dc.degree.departmentInstituto de Químicapt_BR
dc.degree.programCurso de Pós-Graduação em Químicapt_BR
dc.degree.localPorto Alegre, BR-RSpt_BR
dc.degree.date1989pt_BR
dc.degree.levelmestradopt_BR


Files in this item

Thumbnail
   

This item is licensed under a Creative Commons License

Show simple item record