Comparative analysis of the friction and microstructural properties of WC-10Co-4Cr and Cr3C2-25NiCr coatings sprayed by high-velocity oxy-fuel (HVOF)
Fecha
2018Autor
Abstract
In this study, coatings WC-10Co-4Cr and Cr3C2-25NiCr were deposited on the AISI H13 steel by oxy-fuel Thermal spraying (HVOF). This coating increases the wear resistance of surfaces subjected to severe conditions, such as: abrasive wear, thermal fatigue and plastic deformation. The coatings microstructure, hardness and wear resistance are investigated through friction and wear tests performed through a pin-on-disc type tribometer following the procedures defined in ASTM G99-04. It was verified ...
In this study, coatings WC-10Co-4Cr and Cr3C2-25NiCr were deposited on the AISI H13 steel by oxy-fuel Thermal spraying (HVOF). This coating increases the wear resistance of surfaces subjected to severe conditions, such as: abrasive wear, thermal fatigue and plastic deformation. The coatings microstructure, hardness and wear resistance are investigated through friction and wear tests performed through a pin-on-disc type tribometer following the procedures defined in ASTM G99-04. It was verified that both materials used in the spraying have high resistance to wear, however, in the sample coated with Cr3C2-25NiCr there was a greater removal of material during the test. ...
En
American Journal of Materials Science. Rosemead, CA. Vol. 8, no. 3 (2018), p. 51-57
Origen
Estranjero
Colecciones
-
Artículos de Periódicos (39042)Ingeniería (2388)
Este ítem está licenciado en la Creative Commons License