Enhanced damage accumulation in carbon implanted silicon

.

Enhanced damage accumulation in carbon implanted silicon

Mostrar registro completo

Estatísticas

Título Enhanced damage accumulation in carbon implanted silicon
Autor Souza, Joel Pereira de
Boudinov, Henri Ivanov
Fichtner, Paulo Fernando Papaleo
Abstract The accumulation of damage in Si implanted with 12C+ was investigated experimentally using aligned Rutherford backscattering analysis. The damage protiles in Si implanted with 12C+ or 11B+ at 50 keV to the same doses and dose rate were compared. It was found that the damage accumulates at a noticeably higher rate by 12C+ implantation than by 11B+, especially for doses >2X 1Or5 cmm2. In order to explain our results we suggest that self-interstitial Si atoms are captured by the implanted C atoms, forming complex defects which are stable at room temperature.
Contido em Applied physics letters. New York. Vol. 64, no. 26 (June 1994), p. 3596-3597
Assunto Fisica da materia condensada
Implantacao de ions
Retroespalhamento rutherford
Origem Estrangeiro
Tipo Artigo de periódico
URI http://hdl.handle.net/10183/140693
Arquivos Descrição Formato
000220495.pdf (603.1Kb) Texto completo (inglês) Adobe PDF Visualizar/abrir

Este item está licenciado na Creative Commons License

Este item aparece na(s) seguinte(s) coleção(ões)


Mostrar registro completo

Percorrer



  • O autor é titular dos direitos autorais dos documentos disponíveis neste repositório e é vedada, nos termos da lei, a comercialização de qualquer espécie sem sua autorização prévia.
    Projeto gráfico elaborado pelo Caixola - Clube de Criação Fabico/UFRGS Powered by DSpace software, Version 1.8.1.